تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : Ordered Mesoporous Carbon Electrodes for Li-O-2 Batteries Ordered Mesoporous Carbon Electrodes for Li-O-2 Batteries   لغة الوثيقة : الانجليزية  المستخلص : Ordered mesoporous carbon (OMC) with highly ordered pore channels was applied as an oxygen-side electrode for a Li-O-2 battery. To evaluate the effect of the pore channel size on battery performance, we employed OMCs possessing two different pore sizes (6 and 17 nm). When cycled at a current density of 200 mA g(carbon)(-1), the OMC electrodes reduced polarization in the oxygen evolution reaction by 0.1 V compared to those consisting of conventional super P carbon electrode. X-ray diffraction and transmission electron microscopy of the discharged oxygen electrodes provided evidence for the formation of amorphous Li2O2, a product of the oxygen reduction reaction, inside the OMC pores rather than on the electrode surface as in the case of the super P electrode. The OMC electrodes were also effective at high current densities (500 mA g(carbon)(-1) and 1000 mA g(carbon)(-1)).  ردمد : 1944-8244  اسم الدورية : ACS APPLIED MATERIALS & INTERFACES  المجلد : 5  العدد : 24  سنة النشر : 1434 هـ 2013 م  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Sunday, July 16, 2017  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني J Park Park, J باحث     J Lee Lee, J باحث     c Yoon Yoon, c باحث     y Sun Sun, y باحث     الملفات اسم الملف النوع الوصف  42019.pdf pdf   الرجوع إلى صفحة الأبحاث