Reduced graphene oxide decorated with FeF3 nanoparticles: Facile synthesis and application as a high capacity cathode material for rechargeable lithium batteries
Reduced graphene oxide decorated with FeF3 nanoparticles: Facile synthesis and application as a high capacity cathode material for rechargeable lithium batteries
 
لغة الوثيقة : الانجليزية 
المستخلص : n this paper, we demonstrate the preparation of reduced graphene oxide (rGO) decorated with FeF3 nanoparticles (FeF(3)NPs) by adding FeF3 aqueous solution to the rGO ethanol/water dispersion. The obtained FeF3/rGO nanocomposite is further tested as a cathode material for rechargeable lithium batteries and found to have high discharge capacities, good rate capabilities and cycling performance. It can deliver a high discharge capacity of 476 mAh g(-1) at a current density of 50 mAg(-1) in the voltage range 1.0-4.5V. It still delivers a discharge capacity of 146 mAhg(-1) with 81% capacity retention after 50 charge-discharge cycles under a current density of 1000 mAg(-1) in the voltage range 1.7-4.5 V. 
ردمد : 0013-4686 
اسم الدورية : ELECTROCHIMICA ACTA 
المجلد : 111 
العدد : 111 
سنة النشر : 1434 هـ
2013 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, July 17, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
Q ChuChu, Q باحث  
Z XingXing, Z باحث  
x RenRen, X باحث  
A AsiriAsiri, A باحث  
A Alyoubi,Alyoubi,, A باحث  
K AmaryAmary, K باحث  
x sunsun, x باحث  

الملفات

اسم الملفالنوعالوصف
 42041.pdf pdf 

الرجوع إلى صفحة الأبحاث