تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : Characterization of two maritime pine tannins as wood adhesives Characterization of two maritime pine tannins as wood adhesives   لغة الوثيقة : الانجليزية  المستخلص : Maritime pine tannins from the two suppliers BIOLANDES and DRT were used in combination with paraformaldehyde (5%), hexamine (6%) and glyoxal (9%) as hardener in the preparation of adhesives for wood-based panels. Both tannins showed similar structures according to the matrix-assisted laser desorption/ionization-time of flight analysis. A high reactivity has been checked by gel time measurements and the viscosity increase. Already the BIOLANDES and the DRT tannin alone registered an internal bond (IB) of 0.4MPa without any hardener. The BIOLANDES tannin with paraformaldehyde could fulfil the European standard EN 312. In general, DRT tannin obtained the best mechanical results. However, the pH and the moisture content play a fundamental role for the final IB. Thus, DRT tannin with glyoxal as hardener at high pH and moisture content gave an IB of 0.51MPa. The mechanical resistance differences between BIOLANDES and DRT tannin were confirmed by the C-13 NMR spectra. DRT tannin presents a lower polymerization de than BIOLANDES, and more reactive sites are available.  ردمد : 0169-4243  اسم الدورية : JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY  المجلد : 27  العدد : 22  سنة النشر : 1434 هـ 2013 م  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Wednesday, July 19, 2017  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني p Navarrete Navarrete, p باحث     A Pizzi Pizzi, A باحث     H Pasch Pasch, H باحث     K rode rode, K باحث     l Delmotte Delmotte, l باحث     الملفات اسم الملف النوع الوصف  42109.pdf pdf   الرجوع إلى صفحة الأبحاث