Synthesis and characterization of nanoporous silica film via nonsurfactant template solgel technique
Synthesis and characterization of nanoporous silica film via nonsurfactant template solgel technique
 
الموضوع : physics 
لغة الوثيقة : الانجليزية 
المستخلص : Nanoporous silicon dioxide has received growing interests owing to their peculiar application potentials in conservation and storage energy. Therefore, the development of novel and simple techniques is required for raising these nanoporous materials to industrial level. In this research, we report novel strategy for the synthesis of nanoporous SiO2 via nonsurfactant template solgel technique for the first time. The morphology and structure of the as prepared and annealed nanoporous silica films were studied using Xray diffraction, scanning electron microscope. Fourier transform infrared spectroscopy and nitrogen absorption/desorption technique. The results showed that highly order nanoporous silica film has been obtained at annealing temperature 600 degrees C with average diameter 5.1 nm and average pore volume 3.6 cm(3) g(1). ( 
ردمد : 07496036 
اسم الدورية : SUPERLATTICES AND MICROSTRUCTURES 
المجلد : 52 
العدد : 4 
سنة النشر : 1433 هـ
2012 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Saturday, July 22, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
T. (AlHarbi(AlHarbi, T. باحث رئيسيدكتوراه 
F. AlHazmiAlHazmi, F. باحث مشاركدكتوراه 
Waleed E. MahmoudMahmoud, Waleed E. باحث مشاركدكتوراهw_e_mahmoud@yahoo.com

الملفات

اسم الملفالنوعالوصف
 42158.pdf pdf 

الرجوع إلى صفحة الأبحاث