Synthesis, electrical properties and transport mechanisms of thermally vacuum evaporated CdTe nanocrystalline thin films
Synthesis, electrical properties and transport mechanisms of thermally vacuum evaporated CdTe nanocrystalline thin films
 
الموضوع : physics 
لغة الوثيقة : الانجليزية 
المستخلص : A stoichiometry CdTe nano-structured powder was synthesized by chemical process. Thin films of different thicknesses (40, 60, and 100 nm) of CdTe were prepared by thermal evaporation method onto silicon substrates. Current-voltage (I-V) and capacitance-voltage (C-V) characteristics of CdTe nanocrystalline thin films deposited on p-Si as heterojunction have been investigated. At low voltages, current in the forward direction was found to obey the diode equation and the conduction was controlled by thermionic emission mechanism. Also, various electrical parameters were determined from the I-V and C-V analysis. The thickness dependence of the obtained capacitance-voltage (C-V) characteristics was also considered 
ردمد : 0038-1098 
اسم الدورية : SOLID STATE COMMUNICATIONS 
المجلد : 152 
العدد : 17 
سنة النشر : 1433 هـ
2012 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, July 23, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
A.A Al-Ghamdi,Al-Ghamdi, A.A باحث رئيسيدكتوراهaghamdi90@hotmail.com
M. S. Abd El-sadekEl-sadek, M. S. Abd باحث مشاركماجستير 
A.T NagatNagat, A.T باحث مشاركدكتوراه 
F El-TantawyEl-Tantawy, F باحث مشاركدكتوراه 

الملفات

اسم الملفالنوعالوصف
 42196.pdf pdf 

الرجوع إلى صفحة الأبحاث