Synthesis and characterization of AIS chalcopyrite thin films for solar cell applications
Synthesis and characterization of AIS chalcopyrite thin films for solar cell applications
 
الموضوع : physics 
لغة الوثيقة : الانجليزية 
المستخلص : Highly stiochiometric AgInSe2 thin film was prepared on p-type Si (111) substrate via sol-gel spin coating technique. X-ray diffraction spectrum depicted that the crystal structure of AgInSe2 film was chalcopyrite with lattice constants a = 6.102 angstrom and c = 11.69 angstrom. The surface morphology was investigated by a scanning electron microscope (SEM). The results showed that the spherical particles are uniformly distributed with average particle size 23 nm. The current-voltage characteristic curves showed Schottky diode like behavior. The influence of annealing temperatures on the I-V characteristics, photocurrent and solar cell conversion efficiency was examined. The results indicated that the annealing temperature improved the AgInSe2/Si heterostructure photoconductivity properties 
ردمد : 0167-577x 
اسم الدورية : MATERIALS LETTERS 
المجلد : 82 
العدد : 1 
سنة النشر : 1433 هـ
2012 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, July 23, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
F.A Al-AgelAl-Agel, F.A باحث رئيسيدكتوراه 
Waleed E MahmoudMahmoud, Waleed E باحث مشاركدكتوراهw_e_mahmoud@yahoo.com

الملفات

اسم الملفالنوعالوصف
 42198.pdf pdf 

الرجوع إلى صفحة الأبحاث