Structural and magnetic properties of nanocrystalline stannic substituted cobalt ferrite
Structural and magnetic properties of nanocrystalline stannic substituted cobalt ferrite
 
الموضوع : physics 
لغة الوثيقة : الانجليزية 
المستخلص : The structural and magnetic properties of the spinel ferrite system Co1+xFe2-2xSnxO4 (x=0.0-1.0) have been studied. Samples in the series were prepared by the ceramic technique. The structural and microstructural evolutions of the nanophase have been studied using X-ray powder diffraction and the Rietveld method. The refinement result showed that the type of the cationic distribution over the tetrahedral and octahedral sites in the nanocrystalline lattice is partially an inverse spinel. Far infrared absorption spectra show two significant absorption bands, around 600 cm(-1) and 425 cm(-1), which are respectively attributed to tetrahedral (A) and octahedral [B] vibrations of the spinel. Scanning Electron Microscopy (SEM) was used to study surface morphology. SEM images reveal particles in the nanosize range. The transmission electronic microscope (TEM) reveals that the grains are spherical in shape. TEM analysis confirmed the X-ray results. The magnetic properties of the prepared samples were characterized by using a vibrating sample magnetometer. 
ردمد : 0304-8853 
اسم الدورية : JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS 
المجلد : 324 
العدد : 18 
سنة النشر : 1433 هـ
2012 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Sunday, July 23, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
Y.M AbbasAbbas, Y.M باحث رئيسيدكتوراهymabbas@live.com
S.A MansourMansour, S.A باحث مشاركدكتوراه 
M.H IbrahimIbrahim, M.H باحث مشاركدكتوراه 
E. Ali, ShehabAli, Shehab, E. باحث مشاركدكتوراه 

الملفات

اسم الملفالنوعالوصف
 42200.pdf pdf 

الرجوع إلى صفحة الأبحاث