تفاصيل الوثيقة نوع الوثيقة : مقال في مجلة دورية  عنوان الوثيقة : Organic photodetector with coumarin-adjustable photocurrent Organic photodetector with coumarin-adjustable photocurrent   الموضوع : physics  لغة الوثيقة : الانجليزية  المستخلص : Drop casting technique was used to fabricate Al/p-Si/coumarin doped fullerite/Al diodes. The effects of coumarin doping on the photoresponse properties of the diodes were investigated. The forward bias current of the diodes increases exponentially with voltage confirming rectification behavior. The reverse current of the diodes increases with increasing illumination intensities. The photocurrent of the diodes is higher than the dark current. The obtained m value indicates that the photocurrent exhibited a linear photoconducting behavior. The coumarin doped fullerite diodes indicate a non-ideal behavior with obtained ideality factors. The obtained barrier height value of the Al/p-Si/coumarin doped fullerite/Al diode is comparable to that of the conventional Al/p-Si (phi(b) = 0.58 eV) Schottky diode. The measured values of the capacitance decrease with the increasing frequency. The decrease in capacitance was explained on the basis of interface states. It was concluded that the obtained barrier height and interface state density values of the diode are modified doping fullerite with coumarin. The obtained results suggest that the fabricated diodes could be used as an optical sensor in various optoelectronic applications  ردمد : 0379-6779  اسم الدورية : SYNTHETIC METALS  المجلد : 213  العدد : 1  سنة النشر : 1437 هـ 2016 م  نوع المقالة : مقالة علمية  تاريخ الاضافة على الموقع : Monday, August 14, 2017  الباحثون اسم الباحث (عربي) اسم الباحث (انجليزي) نوع الباحث المرتبة العلمية البريد الالكتروني r.o Ocaya Ocaya, r.o باحث رئيسي دكتوراه   A.A Al-Ghamdi, Al-Ghamdi, A.A باحث مشارك دكتوراه   k Mensah-Darkwa Mensah-Darkwa, k باحث مشارك دكتوراه   R.K Gupta, Gupta,, R.K باحث مشارك دكتوراه ramguptamsu@gmail.com F Yakuphanoglu Yakuphanoglu, F باحث مشارك دكتوراه fyhanoglu@firat.edu.tr الملفات اسم الملف النوع الوصف  42608.pdf pdf   الرجوع إلى صفحة الأبحاث