Solution-phase synthesis of chromium-functionalized singlewalled carbon nanotubes
Solution-phase synthesis of chromium-functionalized singlewalled carbon nanotubes
 
الموضوع : physics 
لغة الوثيقة : الانجليزية 
المستخلص : The solution phase reactions of single-walled carbon nanotubes (SWNTs) with Cr(CO)(6) and benzene- Cr (CO)(3) can lead to the formation of small chromium clusters. The cluster size can be varied from less than 1 nm to about 4 nm by increasing the reaction time. TEM images suggest that the clusters are deposited predominantly on the exterior walls of the nanotubes. TGA analysis was used to obtain the Cr content and carbon to chromium ratio in the Cr-complexed SWNTs. It is suggested that the carbon nanotube benzenoid structure templates the condensation of chromium atoms and facilitates the loss of carbon monoxide leading to well defined metal clusters. 
ردمد : 0167-577X 
اسم الدورية : MATERIALS LETTERS 
المجلد : 142 
العدد : 1 
سنة النشر : 1435 هـ
2015 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, August 21, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
I KalininaKalinina, I باحث رئيسيدكتوراه 
Y Al-HadeethiAl-Hadeethi, Y باحث مشاركدكتوراه 
E. BekyarovaBekyarova, E. باحث مشاركدكتوراه 
C ZhaoZhao, C باحث مشاركدكتوراه 
Q WangWang, Q باحث مشاركدكتوراه 
X ZhangZhang, X باحث مشاركدكتوراه 
A AlZahrani,AlZahrani, A باحث مشاركدكتوراه 
F Al-AgelAl-Agel, F باحث مشاركدكتوراه 
F Al-MarzoukiAl-Marzouki,, F باحث مشاركدكتوراه 
R.C HaddonHaddon, R.C باحث مشاركدكتوراهhaddon@ucr.edu

الملفات

اسم الملفالنوعالوصف
 42723.pdf pdf 

الرجوع إلى صفحة الأبحاث