Fabrication of CdMoO4@CdS core-shell hollow superstructures as high performance visible-light driven photocatalysts
Fabrication of CdMoO4@CdS core-shell hollow superstructures as high performance visible-light driven photocatalysts
 
الموضوع : physics 
لغة الوثيقة : الانجليزية 
المستخلص : CdMoO4@CdS core-shell hollow microspheres with the diameter of 2-3 mm were synthesized through a simple ion exchange hydrothermal method by using CdMoO4 solid microspheres as the sacrificial template in the presence of thioacetamide (TAA). Based on the detailed investigation it was found that the concentration of TAA in the starting solution affects the size of the CdS nanosheets and the hollowing process. At the TAA concentration of 0.1 M, CdMoO4@CdS core-shell hollow spheres with a CdS nanosheet thickness of 50-100 nm were obtained. The formed CdS nanosheets have a hexagonal wurtzite structure and exhibit good size uniformity and regularity. Furthermore, the photocatalytic activity of the as-prepared samples was evaluated towards degradation of Rhodomine B (RhB) aqueous dye solution under visible-light. Compared to CdMoO4 microspheres, CdMoO4@CdS coreshell hollow microspheres show enhanced photocatalytic activity. The observed photocatalytic performance was attributed to the synergetic effects of composite morphology, pore structure, and exposed two-dimensional (2D) CdS nanosheets with dominant 001 facets in CdMoO4@CdS core-shell hollow microspheres. Furthermore, the growth mechanism of CdMoO4@CdS hollow microspheres was discussed in detail 
ردمد : 1463-9076 
اسم الدورية : PHYSICAL CHEMISTRY CHEMICAL PHYSICS 
المجلد : 17 
العدد : 23 
سنة النشر : 1435 هـ
2015 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, August 21, 2017 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
P MadhusudanMadhusudan, P باحث رئيسيدكتوراه 
J ZhangZhang, J باحث مشاركدكتوراه 
B ChengCheng, B باحث مشاركدكتوراه 
J.G YuYu, J.G باحث مشاركدكتوراهjphu@iphy.ac.cn

الملفات

اسم الملفالنوعالوصف
 42732.pdf pdf 

الرجوع إلى صفحة الأبحاث